Forming mechanics
of a twin-roll cast AA1100/409L clad sheet after annealing
and cold rolling
Gang Chen, Zonghua Wang and Yuanxin Wang |
|
Vol. 19 (2024), No. 2, 251–264
|
Abstract |
|
Forming mechanics of a twin-roll cast AA1100/409L clad sheet after annealing and cold rolling was investigated by tensile and three-point bending tests. The effect of mechanical properties of the base metals and bonding strength on the strength and ductility of the clad sheet was investigated based on the mixed rule. The clad sheet’s strength obeys the mixed rule only when the bonding strength is as high as 15 N/mm. The negative correlation between strength and ductility and the synergistic effect also exist in the TRC SS/Al clad sheet only when the bonding strength is as high as 15 N/mm. Because of the too small thickness and much higher strength of the steel layer than that of the Al layer, tensile stress dominates during bending of the TRC clad sheet. The deformation and failure process of the clad sheet was analyzed and the processing route for a better formability was proposed. |
PDF Access Denied
We have not been able to recognize your IP address
18.188.103.162
as that of a subscriber to this journal.
Online access to the content of recent issues is by
subscription, or purchase of single articles.
Please contact your institution's librarian suggesting a subscription, for example by using our journal-recommendation form. Or, visit our subscription page for instructions on purchasing a subscription.
You may also contact us at
contact@msp.org
or by using our
contact form.
Or, you may purchase this single article for USD 45.00:
Keywords
twin-roll casting, clad sheet, cold rolling, annealing,
formability
|
Milestones
Received: 28 July 2023
Revised: 14 November 2023
Accepted: 6 December 2023
Published: 31 January 2024
|
Authors |
| Gang Chen | |
| College of Materials Science and
Engineering Qingdao University Qingdao China |
Shool of Electronics
Engineering Guangxi University of Science and Technology Liuzhou China |
| Zonghua Wang | |
| College of Materials Science and
Engineering Qingdao University Qingdao China |
|
| Yuanxin Wang | |
| Zhejiang Hengjiyongxin New Materials
Co. Ningbo China |
|
| © 2024 MSP (Mathematical Sciences Publishers). |