Mechanical
properties of nanocracks in hybrid graphene/hexagonal boron
nitride sheets
Nan Li, Ning Ding, Ting Jiang, Long Liu and Fahmi Zaïri |
|
Vol. 16 (2021), No. 3, 311–326
|
Abstract |
|
Graphene/hexagonal boron nitride (h-BN) is a type of hybrid material to regulate the electronic properties of pristine graphene and is recognized as having potential application in functional devices. Its fracture behavior is one of the most important parameters to affect the device performance. In this work, the fracture behaviors of hybrid graphene/h-BN sheets with cracks were studied using molecular dynamics method. Effects of the crack size, type and location on the failure behavior of the hybrid sheets were considered and analyzed. For most of the models, both Young’s modulus and the fracture strength reduced with the increasing crack size. A threshold of the crack size was found for the models: when the crack size was larger than 0.1 (where is the periodic length of the sheet), Young’s modulus dropped rapidly, while the reduction of the fracture strength slowed down. Crack location had no obvious effect on the fracture strength of the hybrid sheets with a crack of . However, the fracture strength exhibited more dependence on the crack location for a relatively large crack ( or ). The fracture process of the hybrid sheet with a crack usually started from the crack tips where stress concentration existed. If the crack was located in or close to the graphene/h-BN interface, the fracture usually happened in the h-BN domain. The work would provide useful mechanical property information for the applications of hybrid graphene/h-BN sheets in material devices. |
PDF Access Denied
We have not been able to recognize your IP address
18.223.171.12
as that of a subscriber to this journal.
Online access to the content of recent issues is by
subscription, or purchase of single articles.
Please contact your institution's librarian suggesting a subscription, for example by using our journal-recommendation form. Or, visit our subscription page for instructions on purchasing a subscription.
You may also contact us at
contact@msp.org
or by using our
contact form.
Or, you may purchase this single article for USD 45.00:
Keywords
hybrid graphene/hexagonal boron nitride sheet, interface,
nanocrack, fracture, failure
|
Milestones
Received: 16 March 2020
Revised: 4 November 2020
Accepted: 11 January 2021
Published: 2 August 2021
|
Authors |
| Nan Li | |
| Qilu University of Technology
(Shandong Academy of Sciences) Shandong Analysis and Test Center, Qilu University of Technology (Shandong Academy of Sciences), Jin Jinan, 250014 China |
|
| Ning Ding | |
| Qilu University of Technology
(Shandong Academy of Sciences) Shandong Analysis and Test Center, Qilu University of Technology (Shandong Academy of Sciences), Jin Jinan, 250014 China |
|
| Ting Jiang | |
| Qilu University of Technology
(Shandong Academy of Sciences) Shandong Analysis and Test Center, Qilu University of Technology (Shandong Academy of Sciences), Jin Jinan, 250014 China |
|
| Long Liu | |
| Qilu University of Technology
(Shandong Academy of Sciences) Shandong Analysis and Test Center, Qilu University of Technology (Shandong Academy of Sciences), Jin Jinan, 250014 China |
|
| Fahmi Zaïri | |
| Lille University Civil Engineering and geo-Environmental Laboratory, Lille University, Lille 59000, France 59000 Lille France |
|